Effect of Intrinsic Layer Energy Gap and Thicknesses Optimization on the Efficiency of p-i-n Amorphous Silicon Solar Cell

Ignatio Benigno, Darminto Darminto

Abstract


morphous silicon solar cells with single p-i-n layer were grown on 10 cm2 ITO coated glass substrates. Fabrication process done by using 13.56 MHz RF-Plasma Enhanced Chemical Vapor Deposition (PECVD). Hydrogen flow on the deposition process is widely known to enable the passivation of the dangling bond on Silicon bonds. The passivation of dangling bond affects the band gap of each layer and cell performance in the absorption of photon. In the deposition process of intrinsic layer, SiH4 gas flow is set constant at 2.5 sccm, while variation is done in hydrogen gas flow at 0 sccm – 90 sccm. Energy gaps obtained for p-layer and n-layer are 2.0 eV and 2.2 eV at thickness 64 nm and 36 nm respectively. Optimizations have been done for intrinsic layer which band gaps are 1.4 eV, 1.6 eV and 1.9 eV at thickness 400 nm. The solar cell efficiency was increased from 4.8% to 5.64% based on the band gaps variety. In addition, i-layer thicknesses were also varied from 400 nm, 500 nm and 600 nm. Thicknesses variation shows an increase of 5.78% in the solar cell efficiency.

Keywords


Amorphous silicon solar cell; energy gap; efficiency; thicknesses

Full Text:

PDF

References


M. Sharma, S. Juneja, S. Sudhakar, D. Chaudhary, and S. Kumar, “Optimization of a-Si:H absorber layer grown under a low pressure regime by plasma-enhanced chemical vapor deposition: Revisiting the significance of the p/i interface for solar cells,” Mater. Sci. Semicond. Process., vol. 43, pp. 41–46, Mar. 2016.

A. Hajjiah, F. Duerinckx, M. Recamán Payo, I. Kuzma-Filipek, and J. Poortmans, “The effect of surface morphology on the performance of 21% n-type PERT solar cells with an epitaxial rear emitter,” Sol. Energy Mater. Sol. Cells, vol. 151, pp. 139–148, Jul. 2016.

S. Suprianto, “Studi Karakteristik I-V Sel Surya p-i-n Silikon Amorf Terhidrogenasi (a-Si:H),” Institut Teknologi Sepuluh November, 2012.

M. Sharma et al., “Optimization of band gap, thickness and carrier concentrations for the development of efficient microcrystalline silicon solar cells: A theoretical approach,” Sol. Energy, vol. 97, pp. 176–185, Nov. 2013.

Y.-H. Chen, C.-C. Lin, Y.-T. Liu, H.-W. Lu, and J.-C. Liu, “Hydrogen dilution on an undoped silicon oxide layer and Its application to amorphous silicon thin-film solar cells,” Mater. Sci. Semicond. Process., vol. 41, pp. 312–316, Jan. 2016.

J. Poortmans and V. Arkhipov, Thin Film Solar Cells: Fabrication, Characterization and Applications. Chichester, UK: John Wiley & Sons, Ltd, 2006.

D. L. Wood and J. Tauc, “Weak Absorption Tails in Amorphous Semiconductors,” Phys. Rev. B, vol. 5, no. 8, pp. 3144–3151, Apr. 1972.

S. M. Sze and M. K. Lee, Semiconductor devices, physics and technology. New York: Wiley, 2012.

H. P. Zhou, S. Xu, and S. Q. Xiao, “High‐Density Plasma‐Enhanced Chemical Vapor Deposition of Si‐Based Materials for Solar Cell Applications,” in Chemical Vapor Deposition - Recent Advances and Applications in Optical, Solar Cells and Solid State Devices, InTech, 2016.

H. Fujiwara and M. Kondo, “Effects of a‐Si:H layer thicknesses on the performance of a‐Si:H∕c‐Si heterojunction solar cells,” J. Appl. Phys., vol. 101, no. 5, p. 54516, Mar. 2007.




DOI: http://dx.doi.org/10.12962/j23378530.v2i3.a3184

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution 3.0 License.

Visit Statistik : Click Here

Visitor :

Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.