Study of Core Material Sandwich Panel In Ship Construction

Edy Utomo, Achmad Zubaydi, Pompy Pratisna

Abstract


Abstract¾Sandwich panel in ship construction necessitates identification for the core material. Non-metal cores of sandwich materials were identifiedin this study for polyurethane foam, polyresin, and synthetic resin. This material identification was conducted through experiments using Det Norske Veritas (DNV) standard tests. The experiments conducted were reactivity test, density test, and tensile test. Results of the investigation show that the core material suitable for the sandwich panel is synthetic resin with composition of 50% resin,50% talc and 0.3% catalyst. The density of the material is 1,728 kg/m3, tensile strength is 24.75 Mpa, modulus of elastisity is 546.95 Mpa, and shear modulus is 273.48 Mpa.

 


Keywords


Composite material; Polyresin; Polyurethane foam; Sandwich material; Synthetic resin

Full Text:

PDF

References


Moomcilovic and Motok, “Estimation of ship lightweight reduction by means of application of sandwich plate system,” Faculty of Mechanical Engineering, University of Belgrade, Serbia, 2009.

Intelligent Engineering Ltd, “Overlay tanks top plating in plating ship sea princess”, Project Portfolio, IE, UK, 2012.

Brooking and Kennedy, “The performance, safety and production benefits of SPS structures for double hull tankers”, Proceedings of the RINA conference on double hull tankers, pp.1-2, London, UK, 22-26, Feb. 2004.

Baidowi and Utomo, “Penggunaan sandwich plate system (SPS) pada konstruksi double bottom”, e-journal.undip.ac.id, Vol.12, No.2, 2015.

Utomo and Baidowi, “Preliminary study of sandwich panel application in ship construction : combination of plywood and polyurethane foam material”, Proceeding SENTA page 33-38, Faculty of Marine Technology, ITS, Surabaya, Indonesia, 2015.

DNV (Det Norske Veritas), “Steel sandwich pnel construction”, Classification notes for ship, No.30, Nov, 2012.




DOI: http://dx.doi.org/10.12962/j23546026.y2017i2.2304

Refbacks

  • There are currently no refbacks.


View my Stat: Click Here

Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.