The Effect Analysis of Coating Thickness Variation and Mixture Composition of Magnesium – Flake Glass on Epoxy Coating on Abrasive Resistance, Adhesion Strength, and Prediction of Corrosion Rate of ASTM A36 Steel Plate
Abstract
Steel cannot be separated from the marine manufacturing industry. It is important to control the corrosion rate of steel used for offshore structures. The coating method can be used in mobilization areas and splash zones that have high corrosion rates due to sustained friction loads in the marine environment. The purpose of this study was to analyze the different in adhesion strength, abrasion resistance, and corrosion rate prediction of ASTM A36 low carbon steel plate with coating thickness variations of 300µm, 500µm, and 700µm and Magnesium Carbonate - Flake Glass mixture variations of 10%, 20%, and 30%. In the pull-off test, the highest value of adhesion strength was obtained from specimen with 300µm coating thickness and 10% Magnesium Carbonate - Flake Glass mixture with a value of 5.67 Mpa. The highest abrasion test value was obtained from specimen with 700µm coating thickness and 30% Magnesium Carbonate - Flake Glass mixture with a value of 0.91 Wear Cyces per Micrometer. Whereas in the three cells electrode test, the highest value was found at specimen with 700µm coating thickness and 30% Magnesium Carbonate - Flake Glass mixture with a value of 0,00010 mmpy.
Keywords
Full Text:
PDFReferences
Afandi, Y. K.: Analisa Laju Korosi Pada Plat Baja Karbon dengan Variasi Ketebalan Coating. Final Project. Institut Teknologi Sepuluh Nopember. Surabaya. 2015
Ardianto, P. Pengaruh Cacat Coating dan Perbedaan Salinitas Terhadap Laju Korosi Pada Daerah Splash Zone Menggunakan Material Baja ASTM A36. JURNAL TEKNIK ITS Vol. 4, No. 1 ISSN 2337-3539. 2017
ASTM: Standard Test Method for Abrasion Resistance of Organic Coating by the Taber Abraser. D4060-02. ASTM Publishing, Washington. 2010
ASTM: Standard Test Methods for Field Measurement of Surface Profile of Blast Cleaned Steel. D4417. ASTM Publishing, Washington. 1999
ASTM: Pull-off Strength of Coatings Using Portable Adhesion Testers. D4541. ASTM Publishing, Washington. 2002
ASTM: Standard Practice for Calculation of Corrosion Rates and Related Information from Electrochemical Measurements. G102. ASTM Publishing, Washington. 1994
Bagaskoro, M. D. Analisis Tahanan Abrasive dan Kekuatan Adhesi Terhadap Material Baja ASTM A36 Dengan Coating Epoxy dengan Penambahan Flake Glass. Final Project. Institut Teknologi Sepuluh Nopember. Surabaya. 2018
Banerjee, S. Failure Analysis of Resin of Different Coating Materials by Infrared Spectroscopy. International Journal of latest Research in Science and Technology. Volume 3, Issue 3: Page No. 105-108. 2014
Barbhuiya, S. Nanoscale Characterization of Glass Flake Filled Vinyl Ester Ant-Corrotion Coatings. MDPI International Journal. Vol. 7(8): 116. 2017
Bundjali, B. Perilaku dan Inhibisi korosi Baja Karbon Dalam Larutan Buffer Asetat, Bikarbonat-CO2. Dissertations. Institut Teknologi Bandung. Bandung. 2005
Dewi, I.M.S. Studi Perbandingan Laju Korosi Dengan Variasi Cacat Coating Pada Pipa 5L Grade X65 Dengan Media Korosi NaCl. Final Project. Institut Teknologi Sepuluh Nopember. Surabaya. 2011
Fontana and Greene.: Corrosion Engineering International Edition. The Ohio State University. USA. 1987
Gonzales-Guzman, J. Resistance of metallic substates protected by an organic coating containing glass flake. Journal Elsevier B. V. Vol.68:240-243. 2010
Ibrahim, M.C.M. Analisis Pengaruh Variasi Penambahan Kadar Grafit Serbuk Pada Cat Primer Epoxy Terhadap Prediksi Laju Korosi, Kekuatan Adhesi, Dan Metalografi Pada Baja ASTM A36. Final Project. Institut Teknologi Sepuluh Nopember. Surabaya. 2019
ISO: Corrosion Protection of Steel Structures by Painting. 8501. International Organization for Standardization, Geneva. 2011
ISO: Preparation of Steel Subtrates Before Application of Paint and Related Product. 8502. International Organization of Standardization. 2017
Lu, X., Zuo, Y., Zhao, X., Tang, Y. The Improved Performance of a Mgrich Epoxy Coating on AZ91D magnesium alloy by silane pretreatment. Corros. Sci. Vol: 60, 165–172. 2010
Olad, Ali. Preparation of PANI/Epoxy/Zn Nanocomposite using Zn Nanoparticel and Epoxy Resin as Additives and Investigation of Its Corrosion Protection Behavior on Iron. Polymer Composite Research Labolatory: University of Tabriz. 2012
Turel, T., Pathak, S.S., Blanton, M.D., Mendon, S.K., Rawlins, J.W. Optimizing the Transformation of Magnesium Powder to Enhance its Corrosion Protection. In Proceedings of the 38th Annual International Waterborne, High-Solids, and Powder Coatings Symposium, New Orleans, LA, USA. pp. 430–437. 2011
Trethewey KR., Chamberlain J.: KOROSI (Untuk Mahasiswa dan Rekayasawan). PT. Gramedia Pustaka Utama. 1991
DOI: http://dx.doi.org/10.12962%2Fj2580-0914.v4i2.9339
Refbacks
- There are currently no refbacks.