Crystal Structure and Morphology Analysis of Nd1+xBa2−xCu3O7 Oxide Alloy Surface Developed by Solid State Reaction Method

Eko Hadi Sujiono, Husain Ahmad, Fiskia Rera, Samnur Samnur

Abstract


This research has successfully prepared Nd1+xBa2−xCu3O7 oxide alloy which was developed using solid state reaction method with varying molar ratio x = 0.1 to x = 0,3. The process parameter observed was various synthesis routes that were different calcinations temperatures and sintering. In order to acquire the quality of the alloy, the homogeneity of the alloy were analyzed based on the result of EDAX (Energy dispersive X-ray). The composition of the material was analyzed in every variation of synthesis. Last, the crystal and morphology of
Nd1+xBa2−xCu−3O−7 oxide alloy were analyzed based on the result of XRD (x-ray Diffraction) and SEM (Scanning Electron Microscope). The XRD measurements showed that crystal NdBaCuO has been formed. From the results of SEM images also showed that the greater the molar ratio x the particle size will be smaller.

Keywords


solid state reaction; X-Ray diffraction; Scanning Electron Microscope (SEM)

Full Text:

PDF

References


Subaer dan Abdul haris, Fisika material 1 (Badan penerbit universitas negeri makassar, makassar, 2007).

Ismunandar, Padatan oksida logam (Struktur,sintesis, dan sifatsifatnya) (ITB bandung, 2006).

Mitsumasa Suzuki, Preparation and Properties of c-axisoriented Nd1+XBa2−XCu3O7 films by dc Sputtering(1998).

Wickenden,A. E., D. K and Kisthemnacer,T. J., J.Apply.

Physc.75, 5376 (1994).

Y.M.Lu,dkk, Effect Of Rf Power On Optical And Electrical Properties Of ZnO Thin Film By Magnetron Sputtering, Department of electronics engineering (2001).

Adi, Wisnu Ari,dkk, Pengaruh Ukuran Serbuk Terhadap Rapat Arus Kritis Superkonduktor NdBa2Cu3O7−x (2003).




DOI: http://dx.doi.org/10.12962/j24604682.v7i1.893

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.