Study of Morphology of Film Reduced Graphene Oxide from Coconut Shell

Kusuma Wardhani Mas’udah, Fahmi Astuti, Darminto Darminto

Abstract


Coconut shell as the main ingredient in this study were converted into charcoal. The resulted sample coconut shell charcoal was used as a powder and heated. After heating, the powder was dissolved into distilled water. They were coated on the glass substrates using a spin-coating method. Furthermore, this study characterizations using Scanning Electron Microscopy-Energy Dispersive X-ray (SEM-EDX) were conducted for all samples. r-GO layer coconut shell has been successfully made on glass substrates, is shown with layers that have accumulated weight percentage of carbon atoms in each sample layer, that is equal to 84.55% and 20.61%.

Keywords


coconut shell, film r-GO, morphology, spin-coating.

Full Text:

PDF

References


F.M. Wachid, A.Y. Perkasa, F.A. Prasetya, N. Rosyidah, Darminto, “Synthesis and Characterization of Nanocrystalline Graphite from Coconut Shell with Heating Process,” AIP Conf. Proc., 2014.

K.S. Novoselov, et al,”Electric Field Effect in Atomically Thin Carbon Film,”Science 306. Page 666, DOI: 10.1126/science.1102896.

A. K. Geim, K. S. Novoselov, The Rise of Graphene, Nat. Mater. (2007), 6, 183.

K. I. Bolotin, K. J. Sikes, Z. Jiang, M. Klima, G. Fudenberg, J. Hone, P. Kim, H. L. Stormer, Ultrahigh Electron Mobility in Suspended Graphene, Solid State Commun. (2008), 146, 351 .

S. V. Morozov, K. S. Novoselov, M. I. Katsnelson, F. Schedin, D. C. Elias, J. A. Jaszczak, A. K. Geim. Giant Intrinsic Carrier Mobilities in Graphene and Its Bilayer. Phys. Rev. Lett. (2008), 100, 016602 .

A.A. Balandin, S. Ghosh, W.Z. Bao, I. Calizo, D. Teweldebrhan, F. Miao, C.N. Lau. Superior Thermal Conductivity of Single-Layer Graphene. Nano Lett. (2008), 8, 902.

X. Li, Y. Zhu, W. Cai, M. Borysiak, B. Han, D. Chen, R.D. Piner, L. Colombo, R.S. Ruoff. Transfer of Large-Area Graphene Films for High-Performance Transparent Conductive Electrodes. Nano Lett. (2009) , 9 , 4359




DOI: http://dx.doi.org/10.12962/j23546026.y2015i1.1201

Refbacks

  • There are currently no refbacks.


View my Stat: Click Here

Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.