The Influence of SMAW Welding Current Variation on Tensile Strength, Corrosion Rate, and Microstructure of ST 42 Steel for Inner Bottom Plate Material in Ships

Parlindungan Manik, Deddy Chrismianto, Putranda Firman Prayoga

Abstract


Steel is currently widely used in the industrial world. Due to its versatile uses, the development of steel science has also broadened, leading to improved steel processing methods. Welding is a process of joining two pieces of metal using heat. Steel, containing carbon, is prone to oxidation and rust. The aim of this study is to determine the influence of welding current variations on tensile strength, corrosion rate, and the micrographic structure of ST 42 steel. The research method employed is experimental. The welding current variations used are 70 A, 85 A, 100 A, 115 A, and 130 A. In this study, the highest average tensile stress was found at 130 A, measuring 519.20 MPa. For tensile strain, the highest values of 7% were observed at 115 A and 130 A. The highest modulus of elasticity was obtained at 115 A, with a value of 102.18 GPa. The highest corrosion rate occurred in specimens with 70 A, with a value of 0.19 mm/year (good), and the lowest corrosion rate was at 130 A, with a value of 0.10 mm/year (excellent). The micrographic structure testing results showed a decrease in the ferrite phase with each increase in current, while the pearlite phase increased. It can be concluded that the best welding current for ST 42 steel is at 130 A, due to its high tensile strength and low corrosion rate.

Keywords


ST 42 Steel, SMAW Welding, Welding Current Variation, Tensile Strength, Corrosion Rate, Microstructure

Full Text:

PDF

References


H. Pradipta, “Aplikasi Quenching-Tempering Heat Treatment Untuk Meningkatkan Kekuatan Tarik Marine Plat BKI Grade A Pada Material Lambung Kapal Niaga Dengan Variasi Media Pendingin,” J. Tek. Mesin, vol. 6, no. 2, pp. 15–22, 2018.

S. M. M. Rahman, K. E. Karim, and M. H. S. Simanto, “Effect of Heat Treatment on Low Carbon Steel: An Experimental Investigation,” Appl. Mech. Mater., vol. 860, pp. 7–12, Dec. 2016.

A. Hamid, “Analisa Pengaruh Arus Pengelasan SMAW pada Material Baja Karbon Rendah Terhadap Kekuatan Material,” J. Tek. Elektro, vol. 7, no. 2, pp. 14-24, 2016

A. A. Pranata, “Penerapan Perlakuan Panas Quenching-Tempering Dengan Variasi Suhu Pada Material Marine Plat BKI Grade A Di Lambung Kapal Niaga,” J. Tek. Mesin, vol. 6, no. 2, pp. 23–28, 2018.

M. A. F. Pra, “Analisa Kekuatan Tarik, Kekuatan Puntir, Mikrografi, dan Kekerasan Baja ST 41 Sebagai Material Poros Propeller Setelah Proses Quenching dan Tempering,” J. Tek. Perkapalan, vol. 6, no. 4 pp. 19-24, Sep. 2019.

S. A. Mubarok, “Pengaruh Variasi Arus Las SMAW Terhadap Laju Korosi dan Kekuatan Tarik Baja ST 40” J. Tek. Perkapalan, Vol. 09, No. 2, pp 9-11, Apr. 2021”

M. A. Wahyudi, “Analisa Variasi Arus Las SMAW Setelah Proses PWHT Terhadap Kekuatan Tarik, Impak dan Struktur Mikro Pada Baja S50C” J. Tek. Perkapalan, Vol. 03 No. 2, pp.10-11, 2022.

J. G. 4051, “Carbon Steel for Machine Structural Use,” vol. 2016, pp. 1–27,

E. Aprilia, A. Rahmatika, M. Hersaputri, S. Ibrahim, “Studi Awal Pengaruh Variasi Kuat Arus terhadap Kekuatan Tarik Hasil Pengelasan SMAW Material Karbon JIS G3106 dengan Filler E6013,”Jurnal Vokasi Teknologi Industri, vol. 2, no. 1, pp.12-15, 2020.

A. Mustofa, S. Jokosisworo, A. W. B. Santosa “Analisa Kekuatan Tarik, Kekuatan Lentur Putar dan Kekuatan Puntir Baja ST 41 sebagai Bahan Poros Baling-baling Kapal (Propeller Shaft) setelah Proses Quenching,” Jurnal Teknik Perkapalan, vol. 6, no. 1, pp.199-206, 2018.

Suharno, “Struktur Mikro Las Baja C-Mn Hasil Pengelasan Busur Terendam dengan Variasi Masukan Panas,” Jurnal Teknik Mesin, vol. 10, no. 1, pp. 40-46, 2008.

M. A. Wahyudi, “Analisa Variasi Arus Las SMAW Setelah Proses PWHT Terhadap Kekuatan Tarik, Impak dan Struktur Mikro Pada Baja S50C” J. Tek. Perkapalan, Vol. 03 No. 2, pp.10-11, 2022.

S. A. Mubarok, “Pengaruh Variasi Arus Las SMAW Terhadap Laju Korosi dan Kekuatan Tarik Baja ST 40” J. Tek. Perkapalan, Vol. 09, No. 2, pp 9-11, Apr. 2021”

Jones, D.A. “Principles and Prevention of Corrosion”. McMillan Publishing Company. New York, 1991.

F. Nugroho, “Studi Komparasi Pengaruh Variasi Arus Pengelasan Terhadap Kekuatan Impak, Kekerasan, Dan Struktur Mikro Sambungan Las Pegas Daun Baja Sup 9 Pada Proses Las Smaw” J. Tek. Mesin, Vol. 08, No. 3, pp 10-12, Apr. 2020”




DOI: http://dx.doi.org/10.12962/j25481479.v8i2.16900

Refbacks

  • There are currently no refbacks.


Abstracted / Indexed by:
      
  

 

 

 

 

 

P-ISSN: 2541-5972   

E-ISSN: 2548-1479

 

Lisensi Creative Commons

IJMEIR journal published by  Department of Marine Engineering, Faculty of Marine Technology, Institut Teknologi Sepuluh Nopember Surabaya Indonesia under licenced Creative Commons Attribution-ShareAlike 4.0 International Licence. Based on https://iptek.its.ac.id/index.php/ijmeir/