Phase Transformation on Interface between NiCoCrAlY Bond Coat and Substrate and Study of Thermal Barrier Coating as High Temperature Material

H Purwaningsih, L. Noerochim, R. Fajarain, J.A. Hakim, Sulistijono Sulistijono

Abstract


Thermal Barrier Coating material consists of Yttria stabilized zirconia (YSZ) as a top coat and bond coat NiCoCrAlY. It is used to protect NiCoCrAlY super alloys for high temperature applications due to its corrosion resistant properties and resistance to thermal fatigue. In the present study, top coat and bond coat were deposited on the substrate using plasma spraying process, followed by thermal fatigue treatment, by heating up to 900 oC for 5 hours and cooling down to 25 oC for 15 minutes, this process called one cycle. Thermal fatigue was conducted until the material failure. Electron microscope was used to analysis microstructure of the sample after thermal fatigue and x-ray diffraction to analysis phase changed on the interface between bond coat and substrate. The result showed that the specimens failed at 42 cycles (210 hours). A new phase identified as Ni3Al was formed.

Keywords


Thermal fatigue; Phase Transformation; Bond Coat NiCoCrAlY; Substrate NiCoCrAlY

Full Text:

PDF

References


W.J. Quadakkers, V. Shemet, D. Sebold, R. Anton, E. Wessel, L. Singheiser, 2005, “Oxidation characteristics of a platinized MCrAlY bond coat for TBC systems during cyclic oxidation at 1000oC”, Surface & Coatings Technology, Vol. 199, pp. 77-82.

Padture, Amol D. Jadhav, Nitin P, 2007, “Thermal barrier coatings for gas-turbine engine applications”, Science, 296:2002, pp. 280-284

A. Atkinson, J. Williamson, 2007, “Materials for energy”, Materials World, ProQuest Science, pp. 34

S. Bose, dan J. DeMasi-Marcin, 1997, “Thermal barrier coatings experience in gas turbine engines at Pratt &Whitney”, Journal of Thermal Spray Technology, 6(1), pp. 99-104.

J. Ilavsky and J.K. Stalick, Feb 2000, “Phase composition and its changes during annealing of plasma-sprayed YSZ”, Surface & Coatings Technology 127:2000, pp. 121-129.

H.Chen, K. Zhou, Z. Jin, dan C.Liu, 2003, “Diffusion and phase transformation on interface between substrate and NiCrAlY in YPSZ thermal barrier coatings”, Journal of Thermal Spray Technology 13(4), pp. 515-520.

A. A Hesnawi, Hefei Li, Zhaohui Zhou, Shengkai Gong, Huibin Xu, 2007, “Effect of Surface Condition during Pre-Oxidation behavior of MCrAlY bond coat prepared by EB-PVD”, Surface & Coatings Technology, 201, pp. 6793-6796.

Hengbei Zhao, 2006, “Morphology and thermal conductivity of ytria-stabilized zirconia coating”, Acta Materialia 54(2006).




DOI: http://dx.doi.org/10.12962/j20882033.v21i4.89

Refbacks

  • There are currently no refbacks.


Creative Commons License

IPTEK Journal of Science and Technology by Lembaga Penelitian dan Pengabdian kepada Masyarakat, ITS is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Based on a work at https://iptek.its.ac.id/index.php/jts.